Development of a Metal Containing Glass Hollow Fiber Drawing Technique For The Production of Extremely Long Micro/Nanowires
|Zhang et al. report a novel fiber drawing method for forming very long metallic wires with micron to nanometer sized diameters. This method is amenable to scale up for producing vertically aligned arrays of these micro/nanowires in large quantities.|
Reviewed by Dr. Douglas E. Betts, University of North Carolina at Chapel Hill
- Xuejun Zhang, Zeyu Ma, Zhong-Yong Yuam, and Ming Su (2008). “Mass-Productions of Vertically Aligned Extremely Long Metallic Micro/Nanowires Using Fiber Drawing Nanomanufacturing” Advanced Materials 20: 1310-1314. DOI: 10.1002/adma.200702126
The production of ordered arrays of nanometer to micron diameter wires is a challenge by today’s conventional processes using chemical or physical vapor deposition, porous matrices of silica, alumina, or anodized aluminum oxide, or lithographic processes such as photolithography, focused ion beam or electron beam or soft imprint lithography. These techniques suffer from being slow, expensive, and difficult to translate to mass production. Furthermore, they typically result in tangled, horizontally arranged, or surface bonded structures in limited lengths and low yields. Xuejun Zhang and colleagues present in Advanced Materials an ideal method for making wire arrays with nanometer to micron-size diameters in high yields over large areas that can potentially be scaled up to produce vertically aligned micro- or nanowires at meter lengths in large volumes.
In this fiber drawing method a hollow glass tube is first filled with a suitable metal powder. It is important in selecting the glass and the metal powder that the melting point of the metal powder be similar to but not above the drawing temperature of the glass. The filled glass tube is then heated, drawn, cut, and stacked. To prevent oxidation and to make intimate contact between the glass and the filling materials, the glass tube is connected to a vacuum pump and the drawing performed under vacuum. By repeating the process several times the glass tube and fiber diameters are reduced from several millimeters to hundreds of microns. Furthermore, the fibers can be stacked into an array and pulled together to increase throughput and form regular arrays. Once the fibers are formed they are annealed and if desired, the glass may be removed by dissolving in dilute hydrofluoric acid. Using this technique, hexagonal arrays of fibers can be formed as well as individual metal wires of several meters in length. This technique allows for the final designed microwire diameter to be easily calculated from the starting diameter, the draw scaling ratios, and the number of draws. The wires are continuous and very electrically conductive with no oxidation observed.
In practice, it is very important to closely match the melting point of the metal alloy to the drawing temperature of the glass as changes in composition resulting from the evaporation or migration of components in the alloy result in thermophysical and mechanical property changes in the wires that affect the drawing resistance of the glass and the final diameter obtained. Zhang et al. cite examples of micro/nanowires made from copper/phosphor, zinc, and tin with some problems reported but by using glass with the appropriate chemical, thermophysical, and surface properties it should be possible to make large quantities of vertically aligned micro/nanowires of almost any metallic material.
Image from Xuejun Zhang, Zeyu Ma, Zhong-Yong Yuam, and Ming Su (2008). “Mass-Productions of Vertically Aligned Extremely Long Metallic Micro/Nanowires Using Fiber Drawing Nanomanufacturing,” Advanced Materials 2008 (20) 1310-1314. Copyright Wiley-VCH Verlag GmbH & Co. KGaA. Reproduced with permission.
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 3.0 Unported.
Login to add your comment.