Home arrow Resources arrow Expert Reviews arrow Dielectrophoretic Alignment of High Density Carbon Nanotube Arrays

Dielectrophoretic Alignment of High Density Carbon Nanotube Arrays

February 20, 2011
Methods to fabricate 2D arrays of densely packed SWNTs remain an active area of nanomanufacturing research. In this review, a solution-based, post-process has been reported employing AC dielectrophoresis assembly of ultrahigh density SWNT arrays. The versatile approach has demonstrated the highest linear packing density of aligned SWNTs reported to date, with potential impact on the manufacturing of future nanoelectronics.


Reviewed by Jeff Morse, Ph.D., National Nanomanufacturing Network

  • Shekhar S, Stokes P, and Khondaker SI. 2011. Ultrahigh Density Alignment of Carbon Nanotube Arrays by Dielectrophoresis. ACS Nano Article ASAP 16 February 2011. doi: 10.1021/nn102305z

Devices and processes exploiting the properties of carbon nanotubes (CNT) continue to experience notable progress towards applications including transistors, flexible electronics, displays, and sensors. While individual single walled nanotubes (SWNT) exhibit superior electronic transport properties for transistor applications, the ability to control chirality results in large device-to-device performance inhomogeneities. As a result approaches to fabricate CNT transistors have utilized random networks or multilayers of mostly semiconducting SWNTs. While these approaches have been shown to provide homogeneous device characteristics over large areas while enabling high current outputs, charge transport limitations are incurred due to tube-tube junctions within the conduction network. Ultimately such devices could benefit from perfectly aligned two-dimensional (2D) arrays of SWNTs, thereby exhibiting electronic properties approaching the intrinsic properties of the individual nanotubes. As a result, methods to fabricate 2D arrays of densely packed SWNTs remain an active area of nanomanufacturing research. One approach utilizes direct growth on substrates using a patterned catalyst. However, this approach, requires double growth techniques to achieve high densities, as well as high temperature (~900°C) growth and transfer printing steps to transfer the SWNT arrays to suitable device substrates. Ultimately a solution-based, post-growth assembly process would provide a more versatile, lower cost approach for device integration.

Shekar Figure 1
(a) Schematic of the DEP assembly. (b) Two-dimensional simulated electric field around the electrode gap. S and D are Pd source and drain electrodes. (c) Cartoon of the aligned nanotubes after the DEP process. By varying the concentration of SWNT solution, the number density of the assembled nanotubes can be tuned.

Recently, Shekhar et. al. reported on their investigation of AC dielectrophoresis (DEP) as a means to assemble SWNTs with ultrahigh density alignment. As a solution-based process, DEP has the advantage of enabling selected deposition of SWNTs onto prepatterned electrodes without the need for post-processing steps. The authors noted that to achieve effective high-density assembly and alignment, the SWNT suspension must be free of catalytic particles and contain mostly individual SWNTs, as the metallic catalyst particles could potentially migrate into the electrode gap and disrupt the SWNT assembly process. In their approach, the authors utilized a clean, surfactant free, aqueous SWNT suspension, employing the DEP approach to achieve ultrahigh density aligned SWNT arrays. The SWNTs had an average diameter of ~1.7 nm, and varied in length from 0.3-10 µm with a mean length of 1.5 µm as determined by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The original solution contained a SWNT concentration of ~50 µg/mL, and was diluted using deionized water to achieve the desired concentration. Using prepatterned palladium electrodes with gap lengths of 2, 5, and 10 µm, and widths ranging from 25 µm to 1 mm, assembly was achieved by applying an AC voltage of 5 Vp-p at 300 kHz. The solution was applied by casting a 3 µL drop onto the substrate containing the electrodes and applying the AC voltage for 30 seconds which resulted in homogeneous assembly and better reproducibility. Reproducible control of linear array SWNT densities from 0.5 SWNT/µm to >30 SWNT/µm was achieved by variation of the nanotube concentration in the initial solution.

Shekar Figure 2
Scanning electron microscopy (SEM) image for a typical DEP assembly with varying nanotube density: (a) 1 SWNT/¼m; (b) 10 SWNT/¼m; (c) 20 SWNT/¼m; and (d) 30 SWNT/¼m. (e,f) Magnified image of (c) and (d). The nanotube density is varied by simply tuning the concentration of the solution while keeping all other DEP parameters fixed. For this assembly, L = 2 ¼m and W = 25 ¼m.
The authors studied DEP assembly of SWNTs from solutions with concentrations ranging from 0.08 µg/mL to 3.4 µg/mL, with the resulting linear density ranging from 1 SWNT/µm to ~30 SWNT/µm. Key aspects of this technique are that the nanotubes are well-aligned and parallel to each other, particularly at low densities, and that the density of the nanotubes is uniform throughout the width of the electrodes, nominally due to the uniform electric field lines present across such a parallel plate configuration. At higher SWNT concentration in the initial solution, the linear density of the nanotubes did not increase beyond 30/µm, with nanotube separation on the order of 33 nm. For the higher concentrations, nanotube stacking was observed, resulting in 2-3 layers in some locations. It was not clear why the SWNTs could not be more closely packed; this would be an area for further study. The authors were able to demonstrate back-gated transistor operation with the aligned SWNTs after removing the metallic SWNTs bridging the electrodes by applying a large current to effectively burn them out. The transistor On/Off current ratio improved with each voltage sweep to eliminate the metallic conductors in the channel. Reasonable carrier mobilities were observed for the switching transistors, but further study of transistor design and characteristics is required to better understand the transport behavior.

Thus, a solution-based, post-process has been reported employing AC DEP assembly of ultrahigh density SWNT arrays. The versatile approach has demonstrated the highest linear packing density of aligned SWNTs reported to date, with potential impact on the manufacturing of future nanoelectronics.


Images reproduced with permission from Shakar S, Stokes P, and Khondaker SI. 2011. doi: 10.1021/nn102305z. Copyright 2011 American Chemical Society.

Last updated: April 27, 2011
 

DOI: 10.4053/er492-110220

Creative Commons License